烧结钕铁硼性能牌号表

牌号

Br

Hcb

Hcj

(BH)max

TW

 

剩磁

矫顽力

内禀矫顽力

最大磁能积

最高工作

 

 

 

 

 

温度

 

T

KGS

KA/m

KOe

KA/m

KOe

KJ/m3

MGOe

N35

1.17-1.21

11.7-12.1

876-899

11.0-11.3

≥955

≥12

263-279

33-25

≤80

N38

1.22-1.26

12.2-12.6

876-923

11.0-11.6

≥955

≥12

287-303

36-38

≤80

N40

1.26-1.29

12.6-12.9

876-923

11.0-11.6

≥955

≥12

303-318

38-40

≤80

N42

1.30-1.33

13.0-13.3

876-926

11.0-11.6

≥955

≥12

318-334

40-42

≤80

N45

1.33-1.37

13.3-13.7

876-926

11.0-11.6

≥955

≥12

342-358

43-45

≤80

N48

1.36-1.42

13.6-14.2

876-926

11.0-11.6

≥955

≥12

358-382

45-48

≤80

N50

1.41-1.45

14.1-14.5

828-907

10.4-11.4

≥876

≥11

382-398

48-50

≤70

N52

1.44-1.48

14.4-14.8

828-907

10.4-11.4

≥876

≥11

394-414

49.5-52

≤70

N35M

1.17-1.21

11.7-12.1

892-915

11.2-11.5

≥1114

≥14

263-279

33-35

≤100

N38M

1.22-1.26

12.2-12.6

907-931

11.4-11.7

≥1114

≥14

287-303

36-38

≤100

N40M

1.26-1.29

12.6-12.9

907-947

11.4-11.9

≥1114

≥14

303-318

38-40

≤100

N42M

1.30-1.33

13.0-13.3

907-947

11.4-11.9

≥1114

≥14

318-334

40-42

≤100

N45M

1.33-1.37

13.3-13.7

907-955

11.4-12.0

≥1114

≥14

334-358

42-45

≤100

N48M

1.36-1.42

13.6-14.2

907-955

11.4-12.0

≥1114

≥14

358-382

45-48

≤100

N33H

1.14-1.17

11.4-11.7

820-876

10.3-11.0

≥1353

≥17

247-263

31-33

≤120

N35H

1.17-1.21

11.7-12.1

860-907

10.8-11.4

≥1353

≥17

263-279

33-35

≤120

N38H

1.22-1.26

12.2-12.6

907-947

11.4-11.9

≥1353

≥17

287-303

36-38

≤120

N40H

1.26-1.29

12.6-12.9

907-947

11.4-11.9

≥1353

≥17

303-318

38-40

≤120

N42H

1.30-1.33

13.0-13.3

907-947

11.4-11.9

≥1353

≥17

318-334

40-42

≤120

N44H

1.33-1.36

13.3-13.6

907-947

11.4-11.9

≥1274

≥16

334-350

42-44

≤110

N30SH

1.08-1.12

10.8-11.2

804-844

10.1-10.6

≥1592

≥20

223-239

28-30

≤150

N33SH

1.14-1.17

11.4-11.7

820-876

10.3-11.0

≥1592

≥20

247-263

31-33

≤150

N35SH

1.17-1.21

11.7-12.1

860-907

10.8-11.4

≥1592

≥20

263-279

33-35

≤150

N38SH

1.22-1.26

12.2-12.6

907-947

11.4-11.9

≥1592

≥20

287-303

36-38

≤150

N40SH

1.26-1.29

12.6-12.9

907-947

11.4-11.9

≥1592

≥20

303-318

38-40

≤150

N42SH

1.30-1.33

13.0-13.3

907-947

11.4-11.9

≥1512

≥19

318-334

40-42

≤140

N28UH

1.04-1.08

10.4-10.8

780-812

9.8-10.2

≥1990

≥25

207-223

26-28

≤180

N30UH

1.08-1.12

10.8-11.2

804-844

10.1-10.6

≥1990

≥25

223-239

28-30

≤180

N33UH

1.14-1.17

11.4-11.7

820-876

10.3-11.0

≥1990

≥25

247-263

31-33

≤180

N35UH

1.17-1.21

11.7-12.1

860-907

10.8-11.4

≥1990

≥25

263-279

33-35

≤180

N38UH

1.22-1.26

12.2-12.6

860-907

10.8-11.4

≥1990

≥25

287-303

36-38

≤180

N40UH

1.26-1.29

12.6-12.9

860-907

10.8-11.4

≥1990

≥25

289-303

38-40

≤180

N28EH

1.04-1.08

10.4-10.8

780-812

9.8-10.2

≥2388

≥30

207-223

26-28

≤200

N30EH

1.08-1.12

10.8-11.2

804-844

10.1-10.6

≥2388

≥30

223-239

28-30

≤200

N33EH

1.14-1.17

11.4-11.7

820-876

10.3-11.0

≥2388

≥30

247-263

31-33

≤200

N35EH

1.17-1.21

11.7-12.1

860-907

10.8-11.4

≥2388

≥30

263-279

33-35

≤200

N38EH

1.22-1.26

12.2-12.6

860-907

10.8-11.4

≥2388

≥30

287-303

36-38

≤200

热特性

钕铁硼材料类型 热膨胀COEFF。 最大工作温度 居里温度 导热系数
%/℃ °C(°F) °C(°F) 千卡/ MH-℃,
Ñ -0.12 176°F(80℃)下 590°F(310℃) 7.7
NM -0.12 212°F(100℃) 644°F(340°C) 7.7
NH -0.11 248°F(120℃) 644°F(340°C) 7.7
NSH -0.10 302°F(150℃) 644°F(340°C) 7.7
NUH -0.10 356°F(180℃) 662°F(350℃) 7.7
NEH -0.10 392°F(200℃) 662°F(350℃) 7.7



上面列出的热特性通常是与每个磁体的相关联的值等级或材料

物理和机械特性

密度

7.4-7.5克/厘米3

抗压强度

110千克/毫米2

弯曲强度

25公斤/毫米2

维氏硬度(Hv)为

560-600

抗拉强度

7.5公斤/毫米2

杨氏模量

1.7×104千克/毫米2

回复磁导率

1.05μrec

电阻(R)

160μ-欧姆 – 厘米
热容 350-500焦耳/(千克。℃)
热膨胀系数(0〜100°C) 
平行磁化方向
5.2×10 -6 /℃的
热膨胀系数(0〜100°C) 
垂直的磁化方向
-0.8×10 -6 /℃

电镀特性

电镀类型 整体厚度 盐雾试验 压力锅测试
NiCuNi(镍铜镍) 15-21微米 24小时 48小时
铜镍硫化物+黑镍 15-21微米 24小时 48小时
NiCuNi +滴胶 20-28微米 48小时 72小时
NiCuNi +黄金 16-23微米 36小时 72小时
NiCuNi +银 16-23微米 24小时 48小时
7-15微米 12小时 24小时

镍和铜的每一层5-7微米厚。 金银电镀层是1-2微米厚。 

显示测试结果,使镀层选项之间进行比较。 您的特定测试条件下,您的应用性能可能会有所不同。 盐雾试验进行的用5%NaCl溶液,在35℃下。 压力蒸煮试验(PCT)在2个大气压,120℃,100%RH下进行。

测量单位

单位 CGS SI 英文
长度(L)的 厘米(cm)的 米(m) 寸(在)
助焊剂(O) 麦克斯韦 韦伯(WB) 麦克斯韦
磁通密度(B) 高斯(G) 特斯拉(T)的 线/英寸2
磁化力(H) 奥斯特(OE) 安匝数/米(在/ m)的 安匝数/中(在/中)
磁动势(MMF或F) 吉尔伯特(GB) 安匝(At)的 安匝(At)的